Supply PPO plastic materials (PPO) 

 (1) GE PX1005, SE1X-701, SE100X-701, V090, MX4428, HS1000X 

 (2) Japan GE EX130-770, NC208, SE1GFN1-780, GFN1-701 V090-GY71421 

 (3) Asahi Kasei, Japan, 1950J, AS100, X1511, 240Z, X333Z, 340V 

 PPO plastic English name: the poly (phenylene oxide) 

 Specific gravity: 1.07 g / cc mold shrinkage of 0.3 - 0.8% forming temperature :260-290 ℃ dry conditions: 130 ° C for 4 hours 

 Material properties: one for the white particles. Good overall performance, can be used in the 120 degrees of steam, electrical insulation, absorbent, but stress cracking tendency. The Noryl eliminate stress cracking. 

 2, outstanding electrical insulation and water resistance and excellent dimensional stability. Its dielectric properties of ranking the top of the plastic. 3, MPPO the PPO and HIPS blend system modified materials, currently available materials are such materials. 4, a high heat resistance, glass transition temperature of 211 degrees, the melting point of 268 degrees, heated to 330 degrees decomposition tendency, higher PPO content of its better heat resistance, heat distortion temperature of up to 190 degrees. 5, the flame-retardant, self-interest nature, and HIPS mixed with medium flammability. Lightweight, non-toxic can be used in the food and drug industry. Resistant optical activity is poor, a long time in the sun will change. 6, with ABS, HDPE, PPS, PA, HIPS, glass fibers, etc. blending modification. Suitable for production of heat, insulation, anti-friction wear parts, transmission parts, medical and electronic components. 7, gears, blades, valves and other parts for use in high temperature, instead of stainless steel to use. 8, the production of screws, fasteners and fittings. 9, motors, rotors, chassis, transformers, electrical parts. 

 Forming properties: (1) non-crystalline materials, moisture absorption is small. (2) mobility, similar to the Newtonian fluid, the viscosity is more sensitive to temperature, product thickness 0.8 mm. Easy to decompose, the decomposition of corrosive gases. Should be strict control of the molding temperature, the mold should be heated, the gating system is the resistance of the material flow should be. 3, low water absorption of the polyphenylene ether about 0.06%, but trace amounts of moisture will lead to the product surface to the silver and other smooth, it is best for dry processing, the temperature is not higher than 150 degrees, otherwise the color will change. 

 4, the polyphenylene ether of the molding temperature of 280-330 degrees, the Noryl the molding temperature to 260-285 degrees.